Petroleum,petrochemical and natural gas industries —Test methods for quality control  of  microstructure  of  ferritic/austenitic(duplex)stainless  steels

石油、石化和天然气工业铁素体/奥氏体(双相)不锈钢微观结构质量控制的试验方法

1 Scope

1范围

This document specifies quality control testing methods and test conditions for the characterization of  microstructure in relation to relevant properties in

ferritic/austenitic(duplex)stainless  steel  components supplied in the solution annealed condition and fabrication welds in the as welded condition.

本文件规定了在固溶退火条件下供应的铁素体/奥氏体(双相)不锈钢部件和在焊接状态下的制造焊缝的微观结构表征 的质量控制测试方法和测试条件。

This document supplements the relevant product and fabrication standards with respect to destructive

testing methods including sampling of test specimens,test conditions and test acceptance criteria to show freedom from deleterious intermetallic phases and precipitates in duplex stainless steels.In addition,this    document specifies the documentation of testing and test results by the testing laboratory.

本文件补充了有关破坏性测试方法的相关草莓视频下载色和制造标准，包括试样取样、测试条件和测试验收标准，以表明双相不锈钢中没有有害的金属间相和沉淀物。此外，本文件规定了测试实验室的测试和测试结果文件。

NOTE 1:This document is based upon experience with duplex stainless steels in offshore oil and gas industry applications including topside and subsea hydrocarbon service,sea water service,as well as structural use.

注1:本文件基于双相不锈钢在海上石油和天然气行业应用的经验，包括上部和海底碳氢化合物服务、海水服务以及结构用途。

NOTE 2:The austenite spacing is relevant to the susceptibilityof duplex stainless steels to hydrogen-induced

stress cracking(HISC)in subsea applications where cathodic protection is applied.This falls outside the scope of this document.Reference is made to DNV/GL RP-F112 [4].

注2:在采用阴极保护的海底应用中，奥氏体间距与双相不锈钢对氢致应力开裂(HISC)的敏感性有关。这不属于本文件的范围。参考DNV/GLRP-F112[4]。

ISO   148-1,Metallic  materials  —Charpy  pendulum  impact  test—Part  1:Test  method

ISO   148-1,金属材料—夏比摆锤冲击试验—第1部分：试验方法